Ensuring reliability of the rails having corrosionfatigue damages

Data on corrosion fatigue damages of a sole of rails (defect 69) on the railroads of Russia are submitted. It is established that 69 the corrosion fatigue resulting from moistening of a sole in a zone of contact with subrail laying in combination with the high level of the stretching tension in a rail sole is the reason of breaks of rails on defect. The analysis of statistical data on refusals of rails on defect 69 in the West Siberian management of infrastructure showed that failure rate grows to an operating time of the tonnage of 800 million t gross and has fatigue character. On sites of a way with a complicated plan and a profile failure rate is 3 - 4 times higher, than on quiet Trans-Siberian to the course. Results of the analysis of data are shown and measures for increase of reliability of the rail lashes having tendency to formation of defects on a code 69 are offered.